Material Grade Reference Library | Custom Rubber Products

500 manufacturer-listed material grades for reference and comparison.

These are raw-material or compound references, not finished products or confirmed available stock. Reported values are typical source values under the stated test conditions. Blank fields mean not reported; they do not mean zero.

500 matching grades · Page 9 of 20

Manufacturer / grade	Polymer	Hardness	Tensile MPa	Elongation %	Source and test context
Therban® LT 2057 ARLANXEO	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0201 Mooney Viscosity {"value":"67 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"21,0 wt %","test_method":"ISO 24698-1","condition":"","temperature":""} Residual Double Bonds {"value":"5,5 %","test_method":"IR Spectroscopy","condition":"","temperature":""} Density {"value":"0,96 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}
Therban® LT 2157 ARLANXEO	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0202 Mooney Viscosity {"value":"70 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"21,0 wt %","test_method":"ISO 24698-1","condition":"","temperature":""} Residual Double Bonds {"value":"5,5 %","test_method":"IR Spectroscopy","condition":"","temperature":""} Density {"value":"0,96 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}
Therban® LT 2568 ARLANXEO	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0203 Mooney Viscosity {"value":"80 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"25,0 wt %","test_method":"ISO 24698-1","condition":"","temperature":""} Residual Double Bonds {"value":"5,0 %","test_method":"IR Spectroscopy","condition":"","temperature":""} Density {"value":"0,97 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}
Therban® XT VP ARLANXEO	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0204 Mooney Viscosity {"value":"77 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"33,0 wt %","test_method":"ISO 24698-1","condition":"","temperature":""} Residual Double Bonds {"value":"3,5 %","test_method":"IR Spectroscopy","condition":"","temperature":""} Density {"value":"0,97 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}
ZETPOL® 0020 ZEON	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0205 Bound Acrylonitrile [wt %] 49 Mooney Viscosity ML 1+4, 100°C [MU] 58 – 72 Relative Density 1 Iodine value [g/100g] 23
ZETPOL® 1000L ZEON	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0206 Bound Acrylonitrile [wt %] 44 Mooney Viscosity ML 1+4, 100°C [MU] 58 – 72 Relative Density 0,98 Iodine value [g/100g] max. 7
ZETPOL® 1010 ZEON	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0207 Bound Acrylonitrile [wt %] 44 Mooney Viscosity ML 1+4, 100°C [MU] 78 – 92 Relative Density 0,98 Iodine value [g/100g] 10
Zeoforte® ZSC 2095CX ZEON	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0208 Bound Acrylonitrile [wt %] 36¹ Mooney Viscosity ML 1+4, 100°C [MU] 83 - 103 Relative Density 1,24 Iodine value [g/100g] 7¹
Zeoforte® ZSC 2195LCX ZEON	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0209 Bound Acrylonitrile [wt %] 36¹ Mooney Viscosity ML 1+4, 100°C [MU] 55 – 90 Relative Density 1,24 Iodine value [g/100g] 11¹
Zeoforte® ZSC 2295CX ZEON	HNBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0210 Bound Acrylonitrile [wt %] 36¹ Mooney Viscosity ML 1+4, 100°C [MU] 75 – 110 Relative Density 1,24 Iodine value [g/100g] 28¹
X_Butyl® Eco-BC RB 301 ARLANXEO	IIR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0211 Mooney Viscosity {"value":"51 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+8)","temperature":"125 °C"} Antioxidant non-staining {"value":"> 0,03 wt %","test_method":"Internal Method","condition":"","temperature":""} Ash Content {"value":"< 0,3 wt %","test_method":"ISO 247 \/ ASTM D 5667","condition":"","temperature":""} Volatile Content {"value":"< 0,3 wt %","test_method":"ISO 248 \/ ASTM D 5668","condition":"","temperature":""}
X_Butyl® Eco-BC RB 402 ARLANXEO	IIR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0212 Mooney Viscosity {"value":"33 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+8)","temperature":"125 °C"} Antioxidant non-staining {"value":"> 0,03 wt %","test_method":"Internal Method","condition":"","temperature":""} Ash Content {"value":"< 0,3 wt %","test_method":"ISO 247 \/ ASTM D 5667","condition":"","temperature":""}
X_Butyl® RB 101-3 ARLANXEO	IIR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0213 Mooney Viscosity {"value":"51 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+8)","temperature":"125 °C"} Unsaturation {"value":"1,75 %(Mol)","test_method":"(*)","condition":"","temperature":""} Ash Content {"value":"≤ 0,3 wt %","test_method":"ISO 247 \/ ASTM D 5667","condition":"","temperature":""} Volatile Content {"value":"≤ 1 wt %","test_method":"ISO 248 \/ ASTM D 5668","condition":"","temperature":""}
X_Butyl® RB 301 ARLANXEO	IIR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0214 Mooney Viscosity {"value":"51 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+8)","temperature":"125 °C"} Unsaturation {"value":"1,85 %(Mol)","test_method":"(*)","condition":"","temperature":""} Antioxidant non-staining {"value":"> 0,03 wt %","test_method":"Internal Method","condition":"","temperature":""} Ash Content {"value":"≤ 0,3 wt %","test_method":"ISO 247 \/ ASTM D 5667","condition":"","temperature":""} Volatile Content {"value":"≤ 0,3 wt %","test_method":"ISO 248 \/ ASTM D 5668","condition":"","temperature":""}
X_Butyl® RB 402 ARLANXEO	IIR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0215 Mooney Viscosity {"value":"33 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+8)","temperature":"125 °C"} Unsaturation {"value":"2,25 %(Mol)","test_method":"(*)","condition":"","temperature":""} Antioxidant non-staining {"value":"> 0,03 wt %","test_method":"Internal Method","condition":"","temperature":""} Ash Content {"value":"≤ 0,3 wt %","test_method":"ISO 247 \/ ASTM D 5667","condition":"","temperature":""} Volatile Content {"value":"≤ 0,3 wt %","test_method":"ISO 248 \/ ASTM D 5668","condition":"","temperature":""}
NIPOL® IR2200 ZEON	IR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0216 Mooney Viscosity ML 1+4, 100°C [MU] 82
NIPOL® IR2200 L ZEON	IR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0217 Mooney Viscosity ML 1+4, 100°C [MU] 70
Baymod® N 34.52 ARLANXEO	NBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0218 Mooney Viscosity {"value":"45 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"33,0 wt %","test_method":"ISO 24698","condition":"","temperature":""} Density {"value":"0,98 g\/cm3","test_method":"Internal Method","condition":"","temperature":""} Particle Size {"value":"≤ 0,7 mm","test_method":"Internal Method","condition":"","temperature":""}
Baymod® N 34.82 ARLANXEO	NBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0219 Mooney Viscosity {"value":"70 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"33,0 wt %","test_method":"ISO 24698","condition":"","temperature":""} Density {"value":"0,98 g\/cm3","test_method":"Internal Method","condition":"","temperature":""} Particle Size {"value":"0,7 mm","test_method":"Internal Method","condition":"","temperature":""}
Baymod® N XL 33.61 ARLANXEO	NBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0220 Mooney Viscosity {"value":"55 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"33,0 wt %","test_method":"ISO 24698","condition":"","temperature":""} Density {"value":"1,01 g\/cm3","test_method":"Internal Method","condition":"","temperature":""} Particle Size {"value":"0,3 mm","test_method":"Internal Method","condition":"","temperature":""}
Baymod® N XL 33.64 ARLANXEO	NBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0221 Mooney Viscosity {"value":"55 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"33,0 wt %","test_method":"ISO 24698","condition":"","temperature":""} Density {"value":"1,01 g\/cm3","test_method":"Internal Method","condition":"","temperature":""} Particle Size {"value":"0,3 mm","test_method":"Internal Method","condition":"","temperature":""}
Baymod® N XL 38.43 ARLANXEO	NBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0222 Mooney Viscosity {"value":"115 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"38,0 wt %","test_method":"ISO 24698","condition":"","temperature":""} Density {"value":"1,01 g\/cm3","test_method":"Internal Method","condition":"","temperature":""} Particle Size {"value":"0,08 mm","test_method":"Internal Method","condition":"","temperature":""}
Krynac® 2850 F ARLANXEO	NBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0223 Mooney Viscosity {"value":"48 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"27,5 wt %","test_method":"ISO 24698","condition":"","temperature":""} Density {"value":"0,97 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}
Krynac® 2865 F ARLANXEO	NBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0224 Mooney Viscosity {"value":"65 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"28,0 wt %","test_method":"ISO 24698","condition":"","temperature":""} Density {"value":"0,97 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}
Krynac® 33110 F ARLANXEO	NBR	—	—	—	Manufacturer source Reported conditions Accessed 2026-10-19. RSM-0225 Mooney Viscosity {"value":"110 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"} Acrylonitrile Content {"value":"33,0 wt %","test_method":"ISO 24698","condition":"","temperature":""} Density {"value":"0,97 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Source access date: 19 October 2026. Cure conditions are not continuous service-temperature ratings. Shore A and Asker C are kept separate. Refer to the manufacturer source for full conditions and current documentation.