Material Grade Reference Library

Accessed 2026-10-19. RSM-0151

Mooney Viscosity

{"value":"135 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Brookfield Viscosity

{"value":"800 cps","test_method":"ASTM D1417","condition":"","temperature":"25 °C"}

Bound Styrene

{"value":"24,0 wt %","test_method":"ASTM D 5775","condition":"","temperature":""}

Total Solids

{"value":"68,0 wt %","test_method":"ASTM D 1417","condition":"","temperature":""}

Superficial Tension

{"value":"33,5 dyn\/cm","test_method":"ASTM D 1417","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0152

Bound Styrene (%)

23,5

Mooney Viscosity ML 1+4, 100°C [MU]

52

Relative Density

0,94

Antioxidant Type

NS

Accessed 2026-10-19. RSM-0153

Melt Flow Index

{"value":"190 °C 3 g\/10mi","test_method":"ASTM D 1238","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"45 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"0,99 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Particle Size

{"value":"620 µm","test_method":"DIN EN ISO 4610","condition":"","temperature":""}

Separating Agent

{"value":"≤ 0.8 wt % 7 wt %","test_method":"ISO 247 \/ ASTM D 5667","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0154

Melt Flow Index

{"value":"190 °C 4 g\/10mi","test_method":"ASTM D 1238","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"65 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,05 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Particle Size

{"value":"750 µm","test_method":"DIN EN ISO 4610","condition":"","temperature":""}

Separating Agent

{"value":"≤ 0.8 wt % 15 wt %","test_method":"ISO 247 \/ ASTM D 5667","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0155

Melt Flow Index

{"value":"190 °C 3 g\/10mi","test_method":"ISO 1133","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"45 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"0,99 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0156

Melt Flow Index

{"value":"190 °C 10 g\/10mi","test_method":"ISO 1133","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"45 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0157

Melt Flow Index

{"value":"190 °C 25 g\/10mi","test_method":"ISO 1133","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"45 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"0,99 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0158

Melt Flow Index

{"value":"190 °C 2,75 g\/10mi","test_method":"ISO 1133","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"50 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,00 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0159

Melt Flow Index

{"value":"190 °C 2,75 g\/10mi","test_method":"ISO 1133","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"60 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,04 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0160

Melt Flow Index

{"value":"190 °C 25 g\/10mi","test_method":"ISO 1133","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"68 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,06 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0161

Melt Flow Index

{"value":"190 °C 4 g\/10mi","test_method":"ISO 1133","condition":"","temperature":""}

Vinyl Acetate Content

{"value":"70 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,07 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0162

Mooney Viscosity

{"value":"20 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"40 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"0,98 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0163

Mooney Viscosity

{"value":"20 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"45 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"0,99 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0164

Mooney Viscosity

{"value":"27 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"50 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,00 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0165

Mooney Viscosity

{"value":"55 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"50 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,00 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0166

Mooney Viscosity

{"value":"27 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"60 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,04 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0167

Mooney Viscosity

{"value":"55 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"60 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,04 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0168

Mooney Viscosity

{"value":"27 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"70 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,07 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0169

Mooney Viscosity

{"value":"60 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"70 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,07 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0170

Mooney Viscosity

{"value":"28 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"80 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,11 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0171

Mooney Viscosity

{"value":"38 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"90 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,15 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0172

Mooney Viscosity

{"value":"20 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Vinyl Acetate Content

{"value":"60 wt %","test_method":"Internal Method LP 015","condition":"","temperature":""}

Density

{"value":"1,04 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0173

Mooney Viscosity

{"value":"63 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Acrylonitrile Content

{"value":"34 wt %","test_method":"ISO 24698-1","condition":"","temperature":""}

Residual Double Bonds

{"value":"0,9 %","test_method":"IR Spectroscopy","condition":"","temperature":""}

Density

{"value":"0,95 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0174

Mooney Viscosity

{"value":"63 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Acrylonitrile Content

{"value":"34 wt %","test_method":"ISO 24698-1","condition":"","temperature":""}

Residual Double Bonds

{"value":"0,9 %","test_method":"IR Spectroscopy","condition":"","temperature":""}

Density

{"value":"0,95 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}

Accessed 2026-10-19. RSM-0175

Mooney Viscosity

{"value":"70 MU","test_method":"ISO 289 \/ ASTM D 1646","condition":"ML (1+4)","temperature":"100 °C"}

Acrylonitrile Content

{"value":"34,0 wt %","test_method":"ISO 24698-1","condition":"","temperature":""}

Residual Double Bonds

{"value":"0,9 %","test_method":"IR Spectroscopy","condition":"","temperature":""}

Density

{"value":"0,95 g\/cm3","test_method":"Internal Method","condition":"","temperature":""}