Material Grade Reference Library

Accessed 2026-10-19. RSM-0426

Grade and features

Abration resistance

Appearance

Pale yellow

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

Hardness Durometer A

60

Density at 23℃(g/Cm3)

1.15

Linear shrinkage at 150℃

Tensile strength (MPa)

10.0

Elongation at break (%)

605

Tear strength Crescent piece(kN/m)

40

Compression set180℃×22 h(%)

10

Accessed 2026-10-19. RSM-0427

Grade and features

Abration resistance

Appearance

Pale yellow

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

Hardness Durometer A

70

Density at 23℃(g/Cm3)

1.18

Linear shrinkage at 150℃

Tensile strength (MPa)

10.0

Elongation at break (%)

380

Tear strength Crescent piece(kN/m)

30

Compression set180℃×22 h(%)

11

Accessed 2026-10-19. RSM-0428

Grade and features

Abration resistance

Appearance

Pale yellow

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

Hardness Durometer A

80

Density at 23℃(g/Cm3)

1.22

Linear shrinkage at 150℃

Tensile strength (MPa)

9.5

Elongation at break (%)

300

Tear strength Crescent piece(kN/m)

25

Compression set180℃×22 h(%)

13

Accessed 2026-10-19. RSM-0429

Grade and features

Voltage resistance

Appearance

Light gray

Curing agent name

C-3

Standard adding quantity phr

1.3

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

220

Hardness Durometer A

54

Density at 23℃(g/Cm3)

1.15

Linear shrinkage at 150℃

Tensile strength (MPa)

11.0

Elongation at break (%)

780

Tear strength Crescent piece(kN/m)

31

Compression set180℃×22 h(%)

9

Accessed 2026-10-19. RSM-0430

Grade and features

Voltage resistance

Appearance

Gray

Curing agent name

C-3

Standard adding quantity phr

1.3

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

250

Hardness Durometer A

58

Density at 23℃(g/Cm3)

1.20

Linear shrinkage at 150℃

Tensile strength (MPa)

9.2

Elongation at break (%)

680

Tear strength Crescent piece(kN/m)

35

Compression set180℃×22 h(%)

10

Accessed 2026-10-19. RSM-0431

Grade and features

Steam resistance

Appearance

Pale yellow

Curing agent name

C-15

Standard adding quantity phr

1.3

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

220

Hardness Durometer A

55

Density at 23℃(g/Cm3)

1.14

Linear shrinkage at 150℃

3.8

Tensile strength (MPa)

9.5

Elongation at break (%)

410

Tear strength Crescent piece(kN/m)

12

Compression set180℃×22 h(%)

9

Accessed 2026-10-19. RSM-0432

Grade and features

Steam resistance

Appearance

Pale yellow

Curing agent name

C-8A

Standard adding quantity phr

0.6

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

220

Hardness Durometer A

61

Density at 23℃(g/Cm3)

1.15

Linear shrinkage at 150℃

3.9

Tensile strength (MPa)

9.1

Elongation at break (%)

330

Tear strength Crescent piece(kN/m)

11

Compression set180℃×22 h(%)

9

Accessed 2026-10-19. RSM-0433

Grade and features

Heat resistance

Appearance

Pale yellow

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

270

Hardness Durometer A

63

Density at 23℃(g/Cm3)

1.17

Linear shrinkage at 150℃

3.7

Tensile strength (MPa)

10.0

Elongation at break (%)

340

Tear strength Crescent piece(kN/m)

Compression set180℃×22 h(%)

8

Accessed 2026-10-19. RSM-0434

Grade and features

Steam resistance

Appearance

Pale yellow

Curing agent name

C-8A

Standard adding quantity phr

0.6

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

230

Hardness Durometer A

72

Density at 23℃(g/Cm3)

1.21

Linear shrinkage at 150℃

3.9

Tensile strength (MPa)

8.8

Elongation at break (%)

300

Tear strength Crescent piece(kN/m)

15

Compression set180℃×22 h(%)

10

Accessed 2026-10-19. RSM-0435

Grade and features

Heat resistance

Appearance

Grayish white

Curing agent name

C-8

Standard adding quantity phr

1.5

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

370

Hardness Durometer A

83

Density at 23℃(g/Cm3)

1.58

Linear shrinkage at 150℃

2.4

Tensile strength (MPa)

8.5

Elongation at break (%)

110

Tear strength Crescent piece(kN/m)

Compression set180℃×22 h(%)

11

Accessed 2026-10-19. RSM-0436

Grade and features

Oil resistance, solvent resistance

Appearance

Grayish white

Curing agent name

C-8

Standard adding quantity phr

1.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

260

Hardness Durometer A

72

Density at 23℃(g/Cm3)

1.29

Linear shrinkage at 150℃

2.9

Tensile strength (MPa)

6.9

Elongation at break (%)

190

Tear strength Crescent piece(kN/m)

9

Compression set180℃×22 h(%)

10

Accessed 2026-10-19. RSM-0437

Grade and features

General use, conforms to food standards

Appearance

Milky white translucent

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

160

Hardness Durometer A

31

Density at 23℃(g/Cm3)

1.07

Linear shrinkage at 150℃

4.0

Tensile strength (MPa)

4.7

Elongation at break (%)

480

Tear strength Crescent piece(kN/m)

15*

Compression set180℃×22 h(%)

15

Accessed 2026-10-19. RSM-0438

Grade and features

Antistatic

Appearance

Milky white translucent

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

160

Hardness Durometer A

29

Density at 23℃(g/Cm3)

1.09

Linear shrinkage at 150℃

Tensile strength (MPa)

5.5

Elongation at break (%)

600

Tear strength Crescent piece(kN/m)

15*

Compression set180℃×22 h(%)

Accessed 2026-10-19. RSM-0439

Grade and features

General use, conforms to food standards

Appearance

Milky white translucent

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

190

Hardness Durometer A

43

Density at 23℃(g/Cm3)

1.11

Linear shrinkage at 150℃

3.9

Tensile strength (MPa)

6.5

Elongation at break (%)

370

Tear strength Crescent piece(kN/m)

15*

Compression set180℃×22 h(%)

11**

Accessed 2026-10-19. RSM-0440

Grade and features

Dynamic fatigue durability

Appearance

Milky white translucent

Curing agent name

C-8A

Standard adding quantity phr

0.6

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

170

Hardness Durometer A

40

Density at 23℃(g/Cm3)

1.11

Linear shrinkage at 150℃

3.7

Tensile strength (MPa)

6.2

Elongation at break (%)

437

Tear strength Crescent piece(kN/m)

7

Compression set180℃×22 h(%)

8

Accessed 2026-10-19. RSM-0441

Grade and features

Antistatic

Appearance

Milky white translucent

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

190

Hardness Durometer A

43

Density at 23℃(g/Cm3)

1.11

Linear shrinkage at 150℃

Tensile strength (MPa)

6.5

Elongation at break (%)

365

Tear strength Crescent piece(kN/m)

Compression set180℃×22 h(%)

Accessed 2026-10-19. RSM-0442

Grade and features

General use, conforms to food standards

Appearance

Milky white translucent

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

240

Hardness Durometer A

52

Density at 23℃(g/Cm3)

1.14

Linear shrinkage at 150℃

3.9

Tensile strength (MPa)

8.2

Elongation at break (%)

330

Tear strength Crescent piece(kN/m)

23*

Compression set180℃×22 h(%)

11**

Accessed 2026-10-19. RSM-0443

Grade and features

Dynamic fatigue durability

Appearance

Milky white translucent

Curing agent name

C-8A

Standard adding quantity phr

0.6

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

200

Hardness Durometer A

50

Density at 23℃(g/Cm3)

1.12

Linear shrinkage at 150℃

3.3

Tensile strength (MPa)

6.6

Elongation at break (%)

310

Tear strength Crescent piece(kN/m)

6

Compression set180℃×22 h(%)

8

Accessed 2026-10-19. RSM-0444

Grade and features

Antistatic

Appearance

Milky white translucent

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

220

Hardness Durometer A

51

Density at 23℃(g/Cm3)

1.15

Linear shrinkage at 150℃

3.9

Tensile strength (MPa)

8.8

Elongation at break (%)

400

Tear strength Crescent piece(kN/m)

Compression set180℃×22 h(%)

14**

Accessed 2026-10-19. RSM-0445

Grade and features

General use, conforms to food standards

Appearance

Grayish white

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

280

Hardness Durometer A

63

Density at 23℃(g/Cm3)

1.22

Linear shrinkage at 150℃

3.4

Tensile strength (MPa)

7.3

Elongation at break (%)

320

Tear strength Crescent piece(kN/m)

20*

Compression set180℃×22 h(%)

11**

Accessed 2026-10-19. RSM-0446

Grade and features

Dynamic fatigue durability

Appearance

Milky white translucent

Curing agent name

C-8A

Standard adding quantity phr

0.6

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

188

Hardness Durometer A

61

Density at 23℃(g/Cm3)

1.13

Linear shrinkage at 150℃

3.5

Tensile strength (MPa)

7.6

Elongation at break (%)

266

Tear strength Crescent piece(kN/m)

7

Compression set180℃×22 h(%)

5

Accessed 2026-10-19. RSM-0447

Grade and features

General use, conforms to food standards

Appearance

Milky white translucent

Curing agent name

C-8A

Standard adding quantity phr

0.5

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

280

Hardness Durometer A

62

Density at 23℃(g/Cm3)

1.17

Linear shrinkage at 150℃

3.6

Tensile strength (MPa)

9.7

Elongation at break (%)

310

Tear strength Crescent piece(kN/m)

25*

Compression set180℃×22 h(%)

11**

Accessed 2026-10-19. RSM-0448

Grade and features

Antistatic

Appearance

Milky white translucent

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

280

Hardness Durometer A

63

Density at 23℃(g/Cm3)

1.22

Linear shrinkage at 150℃

Tensile strength (MPa)

7.3

Elongation at break (%)

320

Tear strength Crescent piece(kN/m)

Compression set180℃×22 h(%)

Accessed 2026-10-19. RSM-0449

Grade and features

General use, conforms to food standards

Appearance

Grayish white

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

330

Hardness Durometer A

71

Density at 23℃(g/Cm3)

1.30

Linear shrinkage at 150℃

3.0

Tensile strength (MPa)

7.5

Elongation at break (%)

220

Tear strength Crescent piece(kN/m)

20*

Compression set180℃×22 h(%)

9**

Accessed 2026-10-19. RSM-0450

Grade and features

General use, conforms to food standards

Appearance

Milky white translucent

Curing agent name

C-8

Standard adding quantity phr

2.0

Curing conditions(Primary cure)

165℃ × 10 m

Curing conditions(Post cure)

200℃ × 4 h

Williams plasticity(10 min after remix)

340

Hardness Durometer A

71

Density at 23℃(g/Cm3)

1.20

Linear shrinkage at 150℃

3.4

Tensile strength (MPa)

8.8

Elongation at break (%)

260

Tear strength Crescent piece(kN/m)

25*

Compression set180℃×22 h(%)

11**