Material Grade Reference Library

500 manufacturer-listed material grades for reference and comparison.

These are raw-material or compound references, not finished products or confirmed available stock. Reported values are typical source values under the stated test conditions. Blank fields mean not reported; they do not mean zero.

Reset

500 matching grades · Page 15 of 20

Manufacturer / gradePolymerHardnessTensile MPaElongation %Source and test context
KE-2098-40-A/B
Shin-Etsu Chemical		VMQ40 Shore A9.2700Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0351

Grade and features
No post cure (Reduced low-molecular-weight siloxone content), self-adhesive
Appearance
Translucent
Viscosity A/B(Pa・s)
819/797
Curing speed at130℃(MDR)Ｔ10
23
Curing speed at130℃(MDR)Ｔ90
60
Curing conditions(Primary cure)
150℃ × 5 m
Curing conditions(Post cure)
－
Hardness Durometer A
40
Density at 23℃(g/cm3)
1.15
Linear shrinkage at 150℃
2.5
Tensile strength (MPa)
9.2
Elongation at break (%)
700
Tear strength Crescent piece(kN/m)
35
Compression set150℃ × 22 h(%)
－
KE-2098-50-A/B
Shin-Etsu Chemical		VMQ47 Shore A8.5610Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0352

Grade and features
No post cure (Reduced low-molecular-weight siloxone content), self-adhesive
Appearance
Translucent
Viscosity A/B(Pa・s)
890/850
Curing speed at130℃(MDR)Ｔ10
24
Curing speed at130℃(MDR)Ｔ90
54
Curing conditions(Primary cure)
150℃ × 5 m
Curing conditions(Post cure)
－
Hardness Durometer A
47
Density at 23℃(g/cm3)
1.15
Linear shrinkage at 150℃
2.5
Tensile strength (MPa)
8.5
Elongation at break (%)
610
Tear strength Crescent piece(kN/m)
36
Compression set150℃ × 22 h(%)
－
KE-2098-60-A/B
Shin-Etsu Chemical		VMQ61 Shore A8.9430Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0353

Grade and features
No post cure (Reduced low-molecular-weight siloxone content), self-adhesive
Appearance
Translucent
Viscosity A/B(Pa・s)
870/790
Curing speed at130℃(MDR)Ｔ10
22
Curing speed at130℃(MDR)Ｔ90
47
Curing conditions(Primary cure)
150℃ × 5 m
Curing conditions(Post cure)
－
Hardness Durometer A
61
Density at 23℃(g/cm3)
1.14
Linear shrinkage at 150℃
2.5
Tensile strength (MPa)
8.9
Elongation at break (%)
430
Tear strength Crescent piece(kN/m)
42
Compression set150℃ × 22 h(%)
－
KE-2300-12-A/B
Shin-Etsu Chemical		VMQ12 Asker C0.6340Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0354

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
53/53
Curing speed at130℃(MDR)Ｔ10
22
Curing speed at130℃(MDR)Ｔ90
80
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
12*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.6
Elongation at break (%)
340
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
5*8
KE-2300-16-A/B
Shin-Etsu Chemical		VMQ16 Asker C0.6290Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0355

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
51/48
Curing speed at130℃(MDR)Ｔ10
24
Curing speed at130℃(MDR)Ｔ90
78
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
16*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.6
Elongation at break (%)
290
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
4*8
KE-2300-20-A/B
Shin-Etsu Chemical		VMQ20 Asker C0.7250Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0356

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
53/50
Curing speed at130℃(MDR)Ｔ10
22
Curing speed at130℃(MDR)Ｔ90
74
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
20*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.7
Elongation at break (%)
250
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
3*8
KE-2300-24-A/B
Shin-Etsu Chemical		VMQ24 Asker C0.8220Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0357

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
52/46
Curing speed at130℃(MDR)Ｔ10
22
Curing speed at130℃(MDR)Ｔ90
67
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
24*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.8
Elongation at break (%)
220
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
2*8
KE-2300-28-A/B
Shin-Etsu Chemical		VMQ28 Asker C0.8200Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0358

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
55/50
Curing speed at130℃(MDR)Ｔ10
21
Curing speed at130℃(MDR)Ｔ90
66
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
28*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.8
Elongation at break (%)
200
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
2*8
KE-2300-32-A/B
Shin-Etsu Chemical		VMQ32 Asker C0.9190Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0359

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
51/44
Curing speed at130℃(MDR)Ｔ10
20
Curing speed at130℃(MDR)Ｔ90
61
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
32*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.9
Elongation at break (%)
190
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
2*8
KE-2300-36-A/B
Shin-Etsu Chemical		VMQ36 Asker C1180Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0360

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
53/49
Curing speed at130℃(MDR)Ｔ10
22
Curing speed at130℃(MDR)Ｔ90
65
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
36*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
1.0
Elongation at break (%)
180
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
2*8
KE-2300-40-A/B
Shin-Etsu Chemical		VMQ40 Asker C1160Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0361

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
51/47
Curing speed at130℃(MDR)Ｔ10
22
Curing speed at130℃(MDR)Ｔ90
63
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
40*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
1.0
Elongation at break (%)
160
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
2*8
KE-2300-44-A/B
Shin-Etsu Chemical		VMQ44 Asker C1.2150Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0362

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
56/50
Curing speed at130℃(MDR)Ｔ10
23
Curing speed at130℃(MDR)Ｔ90
73
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
44*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
1.2
Elongation at break (%)
150
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
3*8
KE-2300-48-A/B
Shin-Etsu Chemical		VMQ48 Asker C1.4140Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0363

Grade and features
Pressure fixing, insulation
Appearance
Reddish brown
Viscosity A/B(Pa・s)
51/50
Curing speed at130℃(MDR)Ｔ10
22
Curing speed at130℃(MDR)Ｔ90
71
Curing conditions(Primary cure)
120℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Hardness Durometer A
48*7
Density at 23℃(g/cm3)
1.24
Linear shrinkage at 150℃
－
Tensile strength (MPa)
1.4
Elongation at break (%)
140
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
3*8
KE-2310C-08-A/B
Shin-Etsu Chemical		VMQ8 Asker C0.4500Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0364

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
92/89
Curing speed at130℃(MDR)Ｔ10
25
Curing speed at130℃(MDR)Ｔ90
80
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
8*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.4
Elongation at break (%)
500
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
7*8
KE-2310C-12-A/B
Shin-Etsu Chemical		VMQ12 Asker C0.5480Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0365

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
87/86
Curing speed at130℃(MDR)Ｔ10
24
Curing speed at130℃(MDR)Ｔ90
77
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
12*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.5
Elongation at break (%)
480
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
7*8
KE-2310C-16-A/B
Shin-Etsu Chemical		VMQ16 Asker C0.5450Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0366

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
88/87
Curing speed at130℃(MDR)Ｔ10
24
Curing speed at130℃(MDR)Ｔ90
77
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
16*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.5
Elongation at break (%)
450
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
6*8
KE-2310C-20-A/B
Shin-Etsu Chemical		VMQ20 Asker C0.5400Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0367

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
87/86
Curing speed at130℃(MDR)Ｔ10
22
Curing speed at130℃(MDR)Ｔ90
72
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
20*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.5
Elongation at break (%)
400
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
5*8
KE-2310C-24-A/B
Shin-Etsu Chemical		VMQ24 Asker C0.6350Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0368

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
87/84
Curing speed at130℃(MDR)Ｔ10
21
Curing speed at130℃(MDR)Ｔ90
65
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
24*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.6
Elongation at break (%)
350
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
4*8
KE-2310C-28-A/B
Shin-Etsu Chemical		VMQ28 Asker C0.6300Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0369

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
88/83
Curing speed at130℃(MDR)Ｔ10
21
Curing speed at130℃(MDR)Ｔ90
66
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
28*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.6
Elongation at break (%)
300
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
4*8
KE-2310C-32-A/B
Shin-Etsu Chemical		VMQ32 Asker C0.7290Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0370

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
89/84
Curing speed at130℃(MDR)Ｔ10
20
Curing speed at130℃(MDR)Ｔ90
59
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
32*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.7
Elongation at break (%)
290
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
4*8
KE-2310C-36-A/B
Shin-Etsu Chemical		VMQ36 Asker C0.7270Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0371

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
91/85
Curing speed at130℃(MDR)Ｔ10
19
Curing speed at130℃(MDR)Ｔ90
58
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
36*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.7
Elongation at break (%)
270
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
3*8
KE-2310C-40-A/B
Shin-Etsu Chemical		VMQ40 Asker C0.7230Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0372

Grade and features
Pressure fixing, electrical conductivity
Appearance
Black
Viscosity A/B(Pa・s)
87/80
Curing speed at130℃(MDR)Ｔ10
20
Curing speed at130℃(MDR)Ｔ90
60
Curing conditions(Primary cure)
120℃10 m
Curing conditions(Post cure)
200℃4 h
Hardness Durometer A
40*7
Density at 23℃(g/cm3)
1.02
Linear shrinkage at 150℃
－
Tensile strength (MPa)
0.7
Elongation at break (%)
230
Tear strength Crescent piece(kN/m)
－
Compression set150℃ × 22 h(%)
3*8
KE-3502-U
Shin-Etsu Chemical		VMQ51 Shore A6.8345Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0373

Grade and features
Electrical conductivity
Appearance
Black
Curing agent name
C-8A
Standard adding quantity phr
1.0
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
329
Hardness Durometer A
51
Density at 23℃(g/Cm3)
1.10
Linear shrinkage at 150℃
Tensile strength (MPa)
6.8
Elongation at break (%)
345
Tear strength Crescent piece(kN/m)
Compression set180℃×22 h(%)
13
KE-3601SB-U
Shin-Etsu Chemical		VMQ62 Shore A7290Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0374

Grade and features
Electrical conductivity
Appearance
Black
Curing agent name
C-8A
Standard adding quantity phr
1.0
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
450
Hardness Durometer A
62
Density at 23℃(g/Cm3)
1.17
Linear shrinkage at 150℃
4.2
Tensile strength (MPa)
7.0
Elongation at break (%)
290
Tear strength Crescent piece(kN/m)
10
Compression set180℃×22 h(%)
KE-3711-U
Shin-Etsu Chemical		VMQ66 Shore A6.5170Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0375

Grade and features
Electrical conductivity
Appearance
Black
Curing agent name
C-8A
Standard adding quantity phr
1.0
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
480
Hardness Durometer A
66
Density at 23℃(g/Cm3)
1.14
Linear shrinkage at 150℃
Tensile strength (MPa)
6.5
Elongation at break (%)
170
Tear strength Crescent piece(kN/m)
Compression set180℃×22 h(%)
12

Source access date: 19 October 2026. Cure conditions are not continuous service-temperature ratings. Shore A and Asker C are kept separate. Refer to the manufacturer source for full conditions and current documentation.