Material Grade Reference Library

500 manufacturer-listed material grades for reference and comparison.

These are raw-material or compound references, not finished products or confirmed available stock. Reported values are typical source values under the stated test conditions. Blank fields mean not reported; they do not mean zero.

Reset

500 matching grades · Page 12 of 20

Manufacturer / gradePolymerHardnessTensile MPaElongation %Source and test context
NIPOL® DN4555
ZEON		NBR———Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0276

Bound Acrylonitrile [wt %]
45
Mooney Viscosity ML 1+4, 100°C [MU]
48 – 63
Comments
NIPOL®NX 775
ZEON		NBR———Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0277

Comments
Zealloy® 1422A
ZEON		NBR———Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0278

Polymerisation
hot
Bound Acrylonitrile [wt %]
33
Mooney Viscosity ML 1+4, 100°C [MU]
–
Relative Density
0,98
Particle Size [mm]
0,1
Antioxidant Type
NS
NIPOL® NS 540
ZEON		SSBR———Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0279

Bound Styrene (%)
42
Mooney Viscosity ML 1+4, 100°C [MU]
75
NIPOL® NS 612
ZEON		SSBR———Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0280

Bound Styrene (%)
15
Mooney Viscosity ML 1+4, 100°C [MU]
62
NIPOL® NS 616
ZEON		SSBR———Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0281

Bound Styrene (%)
21
Mooney Viscosity ML 1+4, 100°C [MU]
62
FE-221-U
Shin-Etsu Chemical		FVMQ22 Shore A10.3750Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0282

Features
Oil resistance, solvent resistance
Appearance
Milky white translucent
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
230
Hardness Durometer A
22
Density at 23℃(g/cm3)
1.38
Linear shrinkage at 150℃
3.3
Tensile strength(MPa)
10.3
Elongation at break(%)
750
Tear strength Crescent piece(kN/m)
26
Compression set180℃×22 h(%)
11
FE-241-U
Shin-Etsu Chemical		FVMQ43 Shore A9.1470Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0283

Features
Oil resistance, solvent resistance
Appearance
Milky white translucent
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
278
Hardness Durometer A
43
Density at 23℃(g/cm3)
1.38
Linear shrinkage at 150℃
3.7
Tensile strength(MPa)
9.1
Elongation at break(%)
470
Tear strength Crescent piece(kN/m)
14
Compression set180℃×22 h(%)
16
FE-242-U
Shin-Etsu Chemical		FVMQ42 Shore A10300Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0284

Features
Oil resistance, solvent resistance, extrusion
Appearance
Milky white translucent
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
340
Hardness Durometer A
42
Density at 23℃(g/cm3)
1.40
Linear shrinkage at 150℃
3.0
Tensile strength(MPa)
10.0
Elongation at break(%)
300
Tear strength Crescent piece(kN/m)
13
Compression set180℃×22 h(%)
17
FE-2501-U
Shin-Etsu Chemical		FVMQ46 Shore A6.9450Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0285

Features
Oil resistance, solvent resistance, oil breeding
Appearance
Grayish white
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
170℃ × 8分
Curing conditions(Post cure)
Williams plasticity(10 min after remix)
290
Hardness Durometer A
46
Density at 23℃(g/cm3)
1.43
Linear shrinkage at 150℃
2.8
Tensile strength(MPa)
6.9
Elongation at break(%)
450
Tear strength Crescent piece(kN/m)
12
Compression set180℃×22 h(%)
17
FE-251-U
Shin-Etsu Chemical		FVMQ54 Shore A9.8430Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0286

Features
Oil resistance, solvent resistance
Appearance
Pale yellow
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
298
Hardness Durometer A
54
Density at 23℃(g/cm3)
1.41
Linear shrinkage at 150℃
3.5
Tensile strength(MPa)
9.8
Elongation at break(%)
430
Tear strength Crescent piece(kN/m)
15
Compression set180℃×22 h(%)
8
FE-2510-U
Shin-Etsu Chemical		FVMQ53 Shore A9.9320Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0287

Features
Oil resistance, solvent resistance, low compression set
Appearance
Pale yellow
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
283
Hardness Durometer A
53
Density at 23℃(g/cm3)
1.42
Linear shrinkage at 150℃
Tensile strength(MPa)
9.9
Elongation at break(%)
320
Tear strength Crescent piece(kN/m)
10
Compression set180℃×22 h(%)
3
FE-2511-U
Shin-Etsu Chemical		FVMQ50 Shore A9.9433Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0288

Features
Oil resistance, solvent resistance, heat resistance
Appearance
Grayish white
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
306
Hardness Durometer A
50
Density at 23℃(g/cm3)
1.43
Linear shrinkage at 150℃
3.5
Tensile strength(MPa)
9.9
Elongation at break(%)
433
Tear strength Crescent piece(kN/m)
15
Compression set180℃×22 h(%)
7
FE-2513-U
Shin-Etsu Chemical		FVMQ49 Shore A9.9450Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0289

Features
Oil resistance, solvent resistance, heat resistance
Appearance
Red
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
304
Hardness Durometer A
49
Density at 23℃(g/cm3)
1.45
Linear shrinkage at 150℃
4.0
Tensile strength(MPa)
9.9
Elongation at break(%)
450
Tear strength Crescent piece(kN/m)
19
Compression set180℃×22 h(%)
5
FE-261-U
Shin-Etsu Chemical		FVMQ63 Shore A9.8400Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0290

Features
Oil resistance, solvent resistance
Appearance
Pale yellow
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
308
Hardness Durometer A
63
Density at 23℃(g/cm3)
1.42
Linear shrinkage at 150℃
3.5
Tensile strength(MPa)
9.8
Elongation at break(%)
400
Tear strength Crescent piece(kN/m)
16
Compression set180℃×22 h(%)
8
FE-2610-U
Shin-Etsu Chemical		FVMQ63 Shore A10.4270Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0291

Features
Oil resistance, solvent resistance, low compression set
Appearance
Pale yellow
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
296
Hardness Durometer A
63
Density at 23℃(g/cm3)
1.45
Linear shrinkage at 150℃
Tensile strength(MPa)
10.4
Elongation at break(%)
270
Tear strength Crescent piece(kN/m)
11
Compression set180℃×22 h(%)
4
FE-2611-U
Shin-Etsu Chemical		FVMQ57 Shore A8.9410Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0292

Features
Oil resistance, solvent resistance, heat resistance
Appearance
Grayish white
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
309
Hardness Durometer A
57
Density at 23℃(g/cm3)
1.47
Linear shrinkage at 150℃
3.5
Tensile strength(MPa)
8.9
Elongation at break(%)
410
Tear strength Crescent piece(kN/m)
16
Compression set180℃×22 h(%)
7
FE-2613-U
Shin-Etsu Chemical		FVMQ63 Shore A8280Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0293

Features
Oil resistance, solvent resistance, heat resistance
Appearance
Grayish white
Curing agent name
C-8A
Standard adding quantity phr
3.0
Curing conditions(Primary cure)
180℃ × 5 m
Curing conditions(Post cure)
200℃ × 6 h
Williams plasticity(10 min after remix)
329
Hardness Durometer A
63
Density at 23℃(g/cm3)
1.46
Linear shrinkage at 150℃
3.4
Tensile strength(MPa)
8.0
Elongation at break(%)
280
Tear strength Crescent piece(kN/m)
12
Compression set180℃×22 h(%)
7
FE-271-U
Shin-Etsu Chemical		FVMQ73 Shore A9300Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0294

Features
Oil resistance, solvent resistance
Appearance
Grayish white
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
363
Hardness Durometer A
73
Density at 23℃(g/cm3)
1.50
Linear shrinkage at 150℃
3.3
Tensile strength(MPa)
9.0
Elongation at break(%)
300
Tear strength Crescent piece(kN/m)
16
Compression set180℃×22 h(%)
9
FE-2710-U
Shin-Etsu Chemical		FVMQ74 Shore A9.8210Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0295

Features
Oil resistance, solvent resistance, low compression set
Appearance
Pale yellow
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
370
Hardness Durometer A
74
Density at 23℃(g/cm3)
1.48
Linear shrinkage at 150℃
Tensile strength(MPa)
9.8
Elongation at break(%)
210
Tear strength Crescent piece(kN/m)
12
Compression set180℃×22 h(%)
4
FE-273-U
Shin-Etsu Chemical		FVMQ70 Shore A—240Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0296

Features
Oil resistance, solvent resistance, low compression set
Appearance
Grayish white
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
397
Hardness Durometer A
70
Density at 23℃(g/cm3)
1.48
Linear shrinkage at 150℃
3.0
Tensile strength(MPa)
Elongation at break(%)
240
Tear strength Crescent piece(kN/m)
13
Compression set180℃×22 h(%)
5
FE-281-U
Shin-Etsu Chemical		FVMQ80 Shore A7.3150Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0297

Features
Oil resistance, solvent resistance
Appearance
Grayish white
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
403
Hardness Durometer A
80
Density at 23℃(g/cm3)
1.70
Linear shrinkage at 150℃
3.1
Tensile strength(MPa)
7.3
Elongation at break(%)
150
Tear strength Crescent piece(kN/m)
13
Compression set180℃×22 h(%)
15
FE-341-U
Shin-Etsu Chemical		FVMQ38 Shore A13.1630Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0298

Features
Oil resistance, solvent resistance, high strength
Appearance
Pale yellow
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
343
Hardness Durometer A
38
Density at 23℃(g/cm3)
1.42
Linear shrinkage at 150℃
3.3
Tensile strength(MPa)
13.1
Elongation at break(%)
630
Tear strength Crescent piece(kN/m)
32
Compression set180℃×22 h(%)
14
FE-341T-U
Shin-Etsu Chemical		FVMQ42 Shore A12630Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0299

Features
Oil resistance, solvent resistance, translucent
Appearance
Milky white translucent
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
347
Hardness Durometer A
42
Density at 23℃(g/cm3)
1.41
Linear shrinkage at 150℃
3.2
Tensile strength(MPa)
12.0
Elongation at break(%)
630
Tear strength Crescent piece(kN/m)
28
Compression set180℃×22 h(%)
30
FE-343-U
Shin-Etsu Chemical		FVMQ49 Shore A9.6610Manufacturer source
Reported conditions

Accessed 2026-10-19. RSM-0300

Features
Oil resistance, solvent resistance, heat resistance
Appearance
Pale yellow
Curing agent name
C-8A
Standard adding quantity phr
0.8
Curing conditions(Primary cure)
165℃ × 10 m
Curing conditions(Post cure)
200℃ × 4 h
Williams plasticity(10 min after remix)
264
Hardness Durometer A
49
Density at 23℃(g/cm3)
1.38
Linear shrinkage at 150℃
Tensile strength(MPa)
9.6
Elongation at break(%)
610
Tear strength Crescent piece(kN/m)
21
Compression set180℃×22 h(%)
18

Source access date: 19 October 2026. Cure conditions are not continuous service-temperature ratings. Shore A and Asker C are kept separate. Refer to the manufacturer source for full conditions and current documentation.